Powders prepared by melting and sol-gel techniques were processed by cold pressing and sintering to bulk specimens with a well-suited property profile in density and dielectric parameters. Three sets of powder compositions and sintering conditions were selected for substrate preparation. Thin discs (250 and 500 um thickness) were cut from sintered blocks, polished and their metallization behaviour was studied for copper-based microwave lines. Resulting transmission characteristics were measured for coplanar line geometries. Drilling of electrical contact holes was established using a Nd YAG laser.
Several approaches have been established for the sol-gel preparation of cordierite. One procedure was specially adapted to large-scale production (ie quantities above 50 g). The sol-gel technique was also successfully applied for making ferroelectric materials with a wide compositional spectrum available. The technique gives the possibility of obtaining powders and thin films. The qualification of depositing these films on cordierite substrates was demonstrated as well as the principal potential for depositing on other substrates like alumina and silicon.
The processing and characterisation of classical striplines was accomplished by establishing an appropriate thin film Cu metallisation technique for the cordierite substrates. Important high frequency parameters were found to be well predictable by theoretical calculations. Microwave characterisation of the stripline performance was evaluated using simple line geometries, ring resonators and structures in a thin film multi-layer configuration.
The processing and characterisation of substrates with miniaturized elements resulted in a successful implementation of NiCr resistors. Ferroelectric capacitors were formed with the developed sol-gel materials. Stable performance could only be demonstrated for ultra low roughness substrates (silicon).
For integrated circuits, novel composite structures of ceramic substrates and metallic striplines are required to incorporate sub-millimetre size functional elements, especially for uses above 10 GHz. By a Focused Fundamental Research task, it is proposed to demonstrate that alumina substrates can be replaced by reliable alternative low loss dielectrics with substantially lower permittivities (epsilon 5.5) and that as a consequence microwave integrated circuits (MICs) can be realized with enhanced signal transmission characteristics and reduced conductor geometries.
The development focuses on establishing well-controlled processing methods for the (glass-)ceramic and metallic materials involved. The control of the required materials characteristics will be achieved by identifying and understanding the basic features prevailing in the following major processing aspects:
- Densification and concurrent crystallization of highly homogeneous cordierite-based glass powders.
- Microstructural tayloring of the microwave dielectric substrate material
- Formation of MICs with reliably bonded structures by thin film technologies.
- Laser-assisted drilling and metallization of functional holes in MICs.
- Adhesion and structuring of sinteractive capacitive or sensing materials.
The project aims to trigger a subsequent industrial research task oriented to production-adapted processing, which in the long run will strengthen the European position in this key sector of telecommunication systems.
Campo scientifico (EuroSciVoc)
CORDIS classifica i progetti con EuroSciVoc, una tassonomia multilingue dei campi scientifici, attraverso un processo semi-automatico basato su tecniche NLP. Cfr.: Il Vocabolario Scientifico Europeo.
CORDIS classifica i progetti con EuroSciVoc, una tassonomia multilingue dei campi scientifici, attraverso un processo semi-automatico basato su tecniche NLP. Cfr.: Il Vocabolario Scientifico Europeo.
- ingegneria e tecnologia ingegneria dei materiali rivestimenti e pellicole
- ingegneria e tecnologia ingegneria dei materiali solidi amorfi
- scienze naturali matematica matematica pura geometria
- scienze naturali scienze chimiche chimica inorganica metalloidi
- scienze naturali matematica matematica applicata modello matematico
È necessario effettuare l’accesso o registrarsi per utilizzare questa funzione
Siamo spiacenti… si è verificato un errore inatteso durante l’esecuzione.
È necessario essere autenticati. La sessione potrebbe essere scaduta.
Grazie per il tuo feedback. Riceverai presto un'e-mail di conferma dell'invio. Se hai scelto di ricevere una notifica sullo stato della segnalazione, sarai contattato anche quando lo stato della segnalazione cambierà.
Programma(i)
Programmi di finanziamento pluriennali che definiscono le priorità dell’UE in materia di ricerca e innovazione.
Programmi di finanziamento pluriennali che definiscono le priorità dell’UE in materia di ricerca e innovazione.
Argomento(i)
Gli inviti a presentare proposte sono suddivisi per argomenti. Un argomento definisce un’area o un tema specifico per il quale i candidati possono presentare proposte. La descrizione di un argomento comprende il suo ambito specifico e l’impatto previsto del progetto finanziato.
Gli inviti a presentare proposte sono suddivisi per argomenti. Un argomento definisce un’area o un tema specifico per il quale i candidati possono presentare proposte. La descrizione di un argomento comprende il suo ambito specifico e l’impatto previsto del progetto finanziato.
Invito a presentare proposte
Procedura per invitare i candidati a presentare proposte di progetti, con l’obiettivo di ricevere finanziamenti dall’UE.
Dati non disponibili
Procedura per invitare i candidati a presentare proposte di progetti, con l’obiettivo di ricevere finanziamenti dall’UE.
Meccanismo di finanziamento
Meccanismo di finanziamento (o «Tipo di azione») all’interno di un programma con caratteristiche comuni. Specifica: l’ambito di ciò che viene finanziato; il tasso di rimborso; i criteri di valutazione specifici per qualificarsi per il finanziamento; l’uso di forme semplificate di costi come gli importi forfettari.
Meccanismo di finanziamento (o «Tipo di azione») all’interno di un programma con caratteristiche comuni. Specifica: l’ambito di ciò che viene finanziato; il tasso di rimborso; i criteri di valutazione specifici per qualificarsi per il finanziamento; l’uso di forme semplificate di costi come gli importi forfettari.
Coordinatore
76021 Karlsruhe
Germania
I costi totali sostenuti dall’organizzazione per partecipare al progetto, compresi i costi diretti e indiretti. Questo importo è un sottoinsieme del bilancio complessivo del progetto.